Pagrindinis „Chrome Corundum“ turinys

Pagrindinė mineralinė kompozicija yra -al2o 3- cr2O3 kietas sprendimas .
Antrinė mineralinė kompozicija yra nedidelis sudėtinio spinelio kiekis (arba nėra sudėtinio spinelio), o ugniai atspari plyta su chromo oksido kiekiu nuo 1% iki 30% .
Yra dviejų tipų lydytos chromuotos korundum plytos ir sukepintos chromuotos „Corundum“ plytos .
In general, chrome corundum bricks refer to sintered chrome corundum bricks. -Al2O3 is used as the raw material, and an appropriate amount of chromium oxide powder and chrome corundum clinker fine powder are added. After forming, it is fired at high temperature. The chromium oxide content of sintered chrome corundum bricks is generally lower than that of fused chrome corundum bricks. It can also be prepared by mud casting method, -Al2O3 powder and chromium oxide powder are evenly mixed, and a debonding agent and an organic binder are added to make a thick mud. At the same time, part of the chrome corundum clinker is added, and the bricks are made by grouting method, and then Šluostyta . Tai gali būti naudojama kaip stiklinė krosnies pamušalas, nupieštas stiklo srauto skylių dangtelio plyteles ir naudojamas išlydyto geležies išankstinio apdorojimo įrangoje, atliekų deginimo krosnys, vandens kepimo srutų suslėgtos dujinimo krosnies pagrindas ir kt. .